ESAB® AtomArc® 8018 255041816 Low Hydrogen Iron Powder Covered Electrode, 1/8 Inch dia. x 14 Inch L, 50 lb Hermetically Sealed


SKU: WD255041816
$100.00
Weight:
50.00 LBS
Shipping:
Calculated at checkout

  • Image 1

*** CLEARANCE SALE - PRICE GOOD WHILE SUPPLY LASTS***

Item # WD255041816

ESAB® AtomArc® 8018 255041816 Low Hydrogen Iron Powder Covered Electrode, 1/8 Inch dia. x 14 Inch L, 50 lb Hermetically Sealed

Atom Arc 8018 electrodes deposit 1% Ni weld metal. They are used primarily to weld high-tensile steels in the 70-80 ksi (483-552 MPa) tensile strength range, especially where notch toughness at temperatures as low as -40 deg F (-40 deg C) is required

 

Features
  • Moisture resistant coatings are incorporated in all AtomArc® electrodes
  • The flux coatings are manufactured to effectively resist moisture pick-up in opened containers
  • The improved coating provides an extra degree of reliability, especially for electrodes exposed to high humidity environments
  • Flat, horizontal, vertical up, overhead welding positions
  • Medium penetration
  • 2.6 lb/hr at 120 amp, 2.7 lb/hr at 140 amp deposition rate, 71.6% at 120 amp, 70.9% at 140 amp efficiency

 

ESAB® AtomArc® 8018 255041816 Covered Electrode, Diameter: 1/8 Inch, Length: 14 Inch, Current Type: AC/DC+, Amperage: 90 - 160 amp, Package: 50 lb Hermetically Sealed Can, AWS Class: AWS A5.5: E8018-C3, Coating: Low Hydrogen Iron Powder, Tensile Strength: 85 ksi (As Welded), Yield Strength: 74 ksi (As Welded), Elongation in 2" (%): 30% (As Welded), Charpy V-Notch: 124 ft.-lb. At -20 deg F Testing Temperature (As Welded), Welding Process: SMAW (Stick), Weld Metal Composition: 0.046% Carbon (C), 1.11% Manganese (Mn), 0.33% Silicon (Si), 0.011% Phosphorus (P), 0.009% Sulfur (S), 0.97% Nickel (Ni), 0.13% Molybdenum (Mo), Melting Range: >2300 deg F, Applicable Materials: High Tensile Steel